Specification
Brand: As One
Country of Origin: Japan
5-4060-01
- material: zirconia Diameter: �p 0.2 mm Chemical Composition: ZrO 2/95%, Y2O 3/4. 8% Density: 6.0 g/cm 3 Flexural Strength: 1200 MPa Fracture Toughness: 6.0 MPa �� m Torsion Wear Rate: 0.4 ppm/h HV Hardness: 1300 contents amount: 1 kg * Price per 1 kg.
5-4060-02
- material: zirconia Diameter: �p 0.3 mm Chemical Composition: ZrO 2/95%, Y2O 3/4. 8% Density: 6.0 g/cm 3 Flexural Strength: 1200 MPa Fracture Toughness: 6.0 MPa �� m Torsion Wear Rate: 0.4 ppm/h HV Hardness: 1300 contents amount: 1 kg * Price per 1 kg.
5-4060-03
- material: zirconia Diameter: �p 0.4 mm Chemical Composition: ZrO 2/95%, Y2O 3/4. 8% Density: 6.0 g/cm 3 Flexural Strength: 1200 MPa Fracture Toughness: 6.0 MPa �� m Torsion Wear Rate: 0.4 ppm/h HV Hardness: 1300 contents amount: 1 kg * Price per 1 kg.
5-4060-04
- material: zirconia Diameter: �p 0.5 mm Chemical Composition: ZrO 2/95%, Y2O 3/4. 8% Density: 6.0 g/cm 3 Flexural Strength: 1200 MPa Fracture Toughness: 6.0 MPa �� m Torsion Wear Rate: 0.4 ppm/h HV Hardness: 1300 contents amount: 1 kg * Price per 1 kg.
5-4060-05
- material: zirconia Diameter: �p 0.6 mm Chemical Composition: ZrO 2/95%, Y2O 3/4. 8% Density: 6.0 g/cm 3 Flexural Strength: 1200 MPa Fracture Toughness: 6.0 MPa �� m Torsion Wear Rate: 0.4 ppm/h HV Hardness: 1300 contents amount: 1 kg * Price per 1 kg.
5-4060-06
- material: zirconia Diameter: �p 0.65 mm Chemical Composition: ZrO 2/95%, Y2O 3/4. 8% Density: 6.0 g/cm 3 Flexural Strength: 1200 MPa Fracture Toughness: 6.0 MPa �� m Torsion Wear Rate: 0.4 ppm/h HV Hardness: 1300 contents amount: 1 kg * Price per 1 kg.
5-4060-07
- material: zirconia Diameter: �p 0.8 mm Chemical Composition: ZrO 2/95%, Y2O 3/4. 8% Density: 6.0 g/cm 3 Flexural Strength: 1200 MPa Fracture Toughness: 6.0 MPa �� m Torsion Wear Rate: 0.4 ppm/h HV Hardness: 1300 contents amount: 1 kg * Price per 1 kg.
5-4060-08
- material: zirconia Diameter: �p 1 mm Chemical Composition: ZrO 2/95%, Y2O 3/4. 8% Density: 6.0 g/cm 3 Flexural Strength: 1200 MPa Fracture Toughness: 6.0 MPa �� m Torsion Wear Rate: 0.4 ppm/h HV Hardness: 1300 contents amount: 1 kg * Price per 1 kg.
5-4060-09
- material: zirconia Diameter: �p 1.5 mm Chemical Composition: ZrO 2/95%, Y2O 3/4. 8% Density: 6.0 g/cm 3 Flexural Strength: 1200 MPa Fracture Toughness: 6.0 MPa �� m Torsion Wear Rate: 0.4 ppm/h HV Hardness: 1300 contents amount: 1 kg * Price per 1 kg.
5-4060-10
- material: zirconia Diameter: �p 2 mm Chemical Composition: ZrO 2/95%, Y2O 3/4. 8% Density: 6.0 g/cm 3 Flexural Strength: 1200 MPa Fracture Toughness: 6.0 MPa �� m Torsion Wear Rate: 0.4 ppm/h HV Hardness: 1300 contents amount: 1 kg * Price per 1 kg.
5-4060-11
- material: zirconia Diameter: �p 3 mm Chemical Composition: ZrO 2/95%, Y2O 3/4. 8% Density: 6.0 g/cm 3 Flexural Strength: 1200 MPa Fracture Toughness: 6.0 MPa �� m Torsion Wear Rate: 0.4 ppm/h HV Hardness: 1300 contents amount: 1 kg * Price per 1 kg.
5-4060-12
- material: zirconia Diameter: �p 4 mm Chemical Composition: ZrO 2/95%, Y2O 3/4. 8% Density: 6.0 g/cm 3 Flexural Strength: 1200 MPa Fracture Toughness: 6.0 MPa �� m Torsion Wear Rate: 0.4 ppm/h HV Hardness: 1300 contents amount: 1 kg * Price per 1 kg.
5-4060-13
- material: zirconia Diameter: �p 5 mm Chemical Composition: ZrO 2/95%, Y2O 3/4. 8% Density: 6.0 g/cm 3 Flexural Strength: 1200 MPa Fracture Toughness: 6.0 MPa �� m Torsion Wear Rate: 0.4 ppm/h HV Hardness: 1300 contents amount: 1 kg * Price per 1 kg.
5-4060-14
- material: zirconia Diameter: �p 10 mm Chemical Composition: ZrO 2/95%, Y2O 3/4. 8% Density: 6.0 g/cm 3 Flexural Strength: 1200 MPa Fracture Toughness: 6.0 MPa �� m Torsion Wear Rate: 0.4 ppm/h HV Hardness: 1300 contents amount: 1 kg * Price per 1 kg.
5-4060-15
- material: zirconia Diameter: �p 0.05 mm Chemical Composition: ZrO 2/95%, Y2O 3/4. 8% Density: 6.0 g/cm 3 Flexural Strength: 1200 MPa Fracture Toughness: 6.0 MPa �� m Torsion Wear Rate: 0.4 ppm/h HV Hardness: 1300 contents amount: 1 kg * Price per 1 kg.
5-4060-16
- material: zirconia Diameter: �p 0.1 mm Chemical Composition: ZrO 2/95%, Y2O 3/4. 8% Density: 6.0 g/cm 3 Flexural Strength: 1200 MPa Fracture Toughness: 6.0 MPa �� m Torsion Wear Rate: 0.4 ppm/h HV Hardness: 1300 contents amount: 1 kg * Price per 1 kg.
5-4060-17
- material: zirconia Diameter: �p 15 mm Chemical Composition: ZrO 2/95%, Y2O 3/4. 8% Density: 6.0 g/cm 3 Flexural Strength: 1200 MPa Fracture Toughness: 6.0 MPa �� m Torsion Wear Rate: 0.4 ppm/h HV Hardness: 1300 contents amount: 1 kg * Price per 1 kg.
5-4060-18
- material: zirconia Diameter: �p 20 mm Chemical Composition: ZrO 2/95%, Y2O 3/4. 8% Density: 6.0 g/cm 3 Flexural Strength: 1200 MPa Fracture Toughness: 6.0 MPa �� m Torsion Wear Rate: 0.4 ppm/h HV Hardness: 1300 contents amount: 1 kg * Price per 1 kg.
5-4060-19
- material: zirconia Diameter: �p 25 mm Chemical Composition: ZrO 2/95%, Y2O 3/4. 8% Density: 6.0 g/cm 3 Flexural Strength: 1200 MPa Fracture Toughness: 6.0 MPa �� m Torsion Wear Rate: 0.4 ppm/h HV Hardness: 1300 contents amount: 1 kg * Price per 1 kg.
Country of Origin: Japan
5-4060-01
- material: zirconia Diameter: �p 0.2 mm Chemical Composition: ZrO 2/95%, Y2O 3/4. 8% Density: 6.0 g/cm 3 Flexural Strength: 1200 MPa Fracture Toughness: 6.0 MPa �� m Torsion Wear Rate: 0.4 ppm/h HV Hardness: 1300 contents amount: 1 kg * Price per 1 kg.
5-4060-02
- material: zirconia Diameter: �p 0.3 mm Chemical Composition: ZrO 2/95%, Y2O 3/4. 8% Density: 6.0 g/cm 3 Flexural Strength: 1200 MPa Fracture Toughness: 6.0 MPa �� m Torsion Wear Rate: 0.4 ppm/h HV Hardness: 1300 contents amount: 1 kg * Price per 1 kg.
5-4060-03
- material: zirconia Diameter: �p 0.4 mm Chemical Composition: ZrO 2/95%, Y2O 3/4. 8% Density: 6.0 g/cm 3 Flexural Strength: 1200 MPa Fracture Toughness: 6.0 MPa �� m Torsion Wear Rate: 0.4 ppm/h HV Hardness: 1300 contents amount: 1 kg * Price per 1 kg.
5-4060-04
- material: zirconia Diameter: �p 0.5 mm Chemical Composition: ZrO 2/95%, Y2O 3/4. 8% Density: 6.0 g/cm 3 Flexural Strength: 1200 MPa Fracture Toughness: 6.0 MPa �� m Torsion Wear Rate: 0.4 ppm/h HV Hardness: 1300 contents amount: 1 kg * Price per 1 kg.
5-4060-05
- material: zirconia Diameter: �p 0.6 mm Chemical Composition: ZrO 2/95%, Y2O 3/4. 8% Density: 6.0 g/cm 3 Flexural Strength: 1200 MPa Fracture Toughness: 6.0 MPa �� m Torsion Wear Rate: 0.4 ppm/h HV Hardness: 1300 contents amount: 1 kg * Price per 1 kg.
5-4060-06
- material: zirconia Diameter: �p 0.65 mm Chemical Composition: ZrO 2/95%, Y2O 3/4. 8% Density: 6.0 g/cm 3 Flexural Strength: 1200 MPa Fracture Toughness: 6.0 MPa �� m Torsion Wear Rate: 0.4 ppm/h HV Hardness: 1300 contents amount: 1 kg * Price per 1 kg.
5-4060-07
- material: zirconia Diameter: �p 0.8 mm Chemical Composition: ZrO 2/95%, Y2O 3/4. 8% Density: 6.0 g/cm 3 Flexural Strength: 1200 MPa Fracture Toughness: 6.0 MPa �� m Torsion Wear Rate: 0.4 ppm/h HV Hardness: 1300 contents amount: 1 kg * Price per 1 kg.
5-4060-08
- material: zirconia Diameter: �p 1 mm Chemical Composition: ZrO 2/95%, Y2O 3/4. 8% Density: 6.0 g/cm 3 Flexural Strength: 1200 MPa Fracture Toughness: 6.0 MPa �� m Torsion Wear Rate: 0.4 ppm/h HV Hardness: 1300 contents amount: 1 kg * Price per 1 kg.
5-4060-09
- material: zirconia Diameter: �p 1.5 mm Chemical Composition: ZrO 2/95%, Y2O 3/4. 8% Density: 6.0 g/cm 3 Flexural Strength: 1200 MPa Fracture Toughness: 6.0 MPa �� m Torsion Wear Rate: 0.4 ppm/h HV Hardness: 1300 contents amount: 1 kg * Price per 1 kg.
5-4060-10
- material: zirconia Diameter: �p 2 mm Chemical Composition: ZrO 2/95%, Y2O 3/4. 8% Density: 6.0 g/cm 3 Flexural Strength: 1200 MPa Fracture Toughness: 6.0 MPa �� m Torsion Wear Rate: 0.4 ppm/h HV Hardness: 1300 contents amount: 1 kg * Price per 1 kg.
5-4060-11
- material: zirconia Diameter: �p 3 mm Chemical Composition: ZrO 2/95%, Y2O 3/4. 8% Density: 6.0 g/cm 3 Flexural Strength: 1200 MPa Fracture Toughness: 6.0 MPa �� m Torsion Wear Rate: 0.4 ppm/h HV Hardness: 1300 contents amount: 1 kg * Price per 1 kg.
5-4060-12
- material: zirconia Diameter: �p 4 mm Chemical Composition: ZrO 2/95%, Y2O 3/4. 8% Density: 6.0 g/cm 3 Flexural Strength: 1200 MPa Fracture Toughness: 6.0 MPa �� m Torsion Wear Rate: 0.4 ppm/h HV Hardness: 1300 contents amount: 1 kg * Price per 1 kg.
5-4060-13
- material: zirconia Diameter: �p 5 mm Chemical Composition: ZrO 2/95%, Y2O 3/4. 8% Density: 6.0 g/cm 3 Flexural Strength: 1200 MPa Fracture Toughness: 6.0 MPa �� m Torsion Wear Rate: 0.4 ppm/h HV Hardness: 1300 contents amount: 1 kg * Price per 1 kg.
5-4060-14
- material: zirconia Diameter: �p 10 mm Chemical Composition: ZrO 2/95%, Y2O 3/4. 8% Density: 6.0 g/cm 3 Flexural Strength: 1200 MPa Fracture Toughness: 6.0 MPa �� m Torsion Wear Rate: 0.4 ppm/h HV Hardness: 1300 contents amount: 1 kg * Price per 1 kg.
5-4060-15
- material: zirconia Diameter: �p 0.05 mm Chemical Composition: ZrO 2/95%, Y2O 3/4. 8% Density: 6.0 g/cm 3 Flexural Strength: 1200 MPa Fracture Toughness: 6.0 MPa �� m Torsion Wear Rate: 0.4 ppm/h HV Hardness: 1300 contents amount: 1 kg * Price per 1 kg.
5-4060-16
- material: zirconia Diameter: �p 0.1 mm Chemical Composition: ZrO 2/95%, Y2O 3/4. 8% Density: 6.0 g/cm 3 Flexural Strength: 1200 MPa Fracture Toughness: 6.0 MPa �� m Torsion Wear Rate: 0.4 ppm/h HV Hardness: 1300 contents amount: 1 kg * Price per 1 kg.
5-4060-17
- material: zirconia Diameter: �p 15 mm Chemical Composition: ZrO 2/95%, Y2O 3/4. 8% Density: 6.0 g/cm 3 Flexural Strength: 1200 MPa Fracture Toughness: 6.0 MPa �� m Torsion Wear Rate: 0.4 ppm/h HV Hardness: 1300 contents amount: 1 kg * Price per 1 kg.
5-4060-18
- material: zirconia Diameter: �p 20 mm Chemical Composition: ZrO 2/95%, Y2O 3/4. 8% Density: 6.0 g/cm 3 Flexural Strength: 1200 MPa Fracture Toughness: 6.0 MPa �� m Torsion Wear Rate: 0.4 ppm/h HV Hardness: 1300 contents amount: 1 kg * Price per 1 kg.
5-4060-19
- material: zirconia Diameter: �p 25 mm Chemical Composition: ZrO 2/95%, Y2O 3/4. 8% Density: 6.0 g/cm 3 Flexural Strength: 1200 MPa Fracture Toughness: 6.0 MPa �� m Torsion Wear Rate: 0.4 ppm/h HV Hardness: 1300 contents amount: 1 kg * Price per 1 kg.